Technical Data & Safety Information
Your resource for technical specifications and Material Safety & Data Sheet (MSDS) information.
| ProCote Bond/Base Series II |
|
ProCote Bond/Base Series II is an environmentally acceptable catalyzed epoxy coating system. The chemical properties of the materials react to harden not only on, but into the concrete producing a plastic-like finish. This water-based, three-part component system is applied over dampened concrete ensuring penetration and adhesion. Integral film properties are obtained after curing of the mixed components. Pigmentation is accomplished using quality colorants known to resist chemical degradation. Proper levels of pigmentation are maintained to insure good hiding and gloss control.
| PHYSICAL CHARACTERISTICS |
Abrasion Resistance
Tabor Abrasor using CS-17 calibrase wheel with 1000 gram total load for 500 cycles |
54 mg loss |
Flexibility
1/8" mandrel |
No cracks |
Impact Resistance
Gardiner Variable Impactor (passed) |
|
Adhesion
No delamination (concrete failure) |
425 p.s.i.
with alcometer
|
Pot Life
|
90 mins
at 68° F |
Cure Schedule
Temperature at 68° F |
4-6 hours to Tack-Free
5-7 hours to Recoat
2-7 days to Full Cure
|
| SPECIFYING INFORMATION |
Volatile Organic Content (VOC)
|
Part A: 1.20 lbs/gal
Part B: 0.0 lbs/gal
Mixed: 1.01 lbs/gal |
Solids by Volume
|
|
Solids by Weight
|
|
Finish Characteristics
|
|
Mix Ratio
|
|
Thickness
per coat |
5-7 mils wet
2-3 mils dry
|
| CHEMICAL RESISTANCE |
KEY: R=RECOMMENDED FOR IMMERSION SERVICE; RS=RECOMMENDED FOR SPILLAGE ONLY; NR=NOT RECOMMENDED
ALKALIES
| Sodium Hydroxide (dilute) |
R |
| Sodium Hydroxide (concentrate) |
R |
| Calcium Hydroxide |
R |
| Ammonium Hydroxide (dilute) |
R |
| Ammonium Hydroxide (concentrate) |
RS |
| Ammonium Salts |
R |
| Sodium Carbonate |
R |
| |
|
ACIDS
| Sulfuric (10%) |
NR |
| Sulfuric (concentrate) |
NR |
| Hydrochloric (10%) |
RS |
| Hydrochloric (concentrate) |
RS |
| Nitric (10%) |
RS |
| Nitric (concentrate) |
NR |
| Phosphoric (10%) |
RS |
| Phosphoric (concentrate) |
NR |
| Hydrofluoric (10%) |
RS |
| Hydrofluoric (30%) |
NR |
| Lower Fatty, e.g. Acetic (20%) |
NR |
| Lower Fatty, e.g. Acetic (concentrate) |
NR |
| High Fatty, e.g. Oleic |
NR |
| Organic Food, e.g. Citric |
R |
| |
|
SOLVENTS
| Methylene Chloride |
NR |
| Other Chlorinated Hydrocarbons |
RS |
| Aromatic Hydrocarbons |
R |
| Aliphatic Hydrocarbons |
R |
| Alcohol (Methyl, Ethyl, & Butyl) |
R |
| Ether |
R |
| Esters |
RS |
| Ketones |
RS |
| Phenol |
RS |
| "Skydrol 500" |
R |
| |
|
HALOGENS
| Chloride |
NR |
| Bromine |
NR |
| Iodine |
NR |
| |
|
|
|
OXIDIZING AGENTS
| Hydrogen Peroxide (30%) |
NR |
| Sodium Hypochlorite (5%) |
R |
| Calcium Hypochlorite (5%) |
R |
| Chromic Acid (40%) |
NR |
| Chromic Acid (5%) |
NR |
| Sodium Dioxide Solutions |
NR |
| Chlorine Water |
R |
| |
|
WATER
SALT SOLUTIONS (5%-10%)
| Alum |
R |
| Ferrous Sulfate |
R |
| Copper Sulfate |
R |
| Sodium Chloride |
R |
| Calcium Chloride |
R |
| Sodium Sulfate |
R |
| Sodium Phosphate |
R |
| Sodium Acetate |
R |
| |
|
FATS AND OILS
| Mineral |
RS |
| Animal |
RS |
| Vegetable |
RS |
| |
|
GASES (MOIST)
| Carbon Dioxide |
R |
| Sulfur Dioxide |
R |
| Hydrogen Sulfide |
R |
| |
|
|
|
| RECOMMENDED USES |
This system is primarily used for those applications where coatings must exhibit superior resistance to chemical exposure. Additionally, ProCote I is noted for outstanding adhesion to various types of substrates, demonstrating flexible toughness, impact and adrasion resistance. |
| NOT RECOMMENDED FOR |
This system is not recommended for exterior use where early "chalking" and loss of gloss is deemded undesirable. |
| INSTALLATION |
Installation is performed exclusively by our own factory-trained staff. Areas to be coated must be free of dirt, grease, oil, wax, and stripped of all previously applied coatings, sealants and curing compounds that are incompatible with this product. The application of a top coat is recommended to ensure proper sealing of the surface to be coated. |
|
| ProCote Bond/Base 2000 |
|
ProCote Bond/Base 2000 is a high-build, self-leveling epoxy floor coating. The material pours down and spreads out to smooth over rough, damaged or worn concrete surfaces. It provides greater resistance to heavy-duty use in mechanical areas or porfessional repair facilities. ProCote Bond/Base 2000 is available in clear and a variety of colors.
| PHYSICAL CHARACTERISTICS |
Abrasion Resistance
Tabor Abrasor using CS-17 calibrase wheel with 1000 gram total load for 500 cycles |
|
Flexural Strength
½" x ½" bars / span 4" |
|
Impact Resistance
Gardiner Variable Impactor (passed) |
50 in/lb
direct |
Yield Compressive Strength
½" x ½" bars |
9100 p.s.i.
@ASTM D695 |
Tensile Strength
Testing directions: F=2.25", W=0.500", T=0.125", D=4.5" | Rate: 0.2"/min |
4800 p.s.i.
@ASTM D638 |
Ultimate Elongation |
3.1% |
Hardness |
Shore D=80 |
Adhesion
No delamination (concrete failure) |
450 p.s.i.
with alcometer |
Application Temperature |
60-90° F
with relative humidity < 85% |
Viscosity
Typical, most colors |
1300-2300 cps
|
Pot Life |
30-50 mins
at 70° F |
Cure Schedule
Temperature at 70° F |
5-8 hours to Tack-Free
8-12 hours to Recoat
2-7 days to Full Cure |
| SPECIFYING INFORMATION |
Volatile Organic Content (VOC) |
Nearly zero pounds per gallon |
Solids by Volume |
|
Solids by Weight |
|
Finish Characteristics
Erichsen glossmeter |
Gloss
70-95 at 60° |
| Mix Ratio |
2 : 1
Part A : Part B |
Recommended Film Thickness |
12-30 mils |
| CHEMICAL RESISTANCE |
RATING KEY
| NOT RECOMMENDED |
A |
| 2 HR TERM SPLASH SPILL |
B |
| 8 HR TERM SPLASH SPILL |
C |
| 72 HOUR IMMERSION |
D |
| LONG TERM IMMERSION |
E |
| |
|
|
|
| Xylene |
C |
| Trichloroethane |
B |
| Methanol |
A |
| Ethyl Alcohol |
B |
| Skydrol |
B |
| Sodium Hydroxide (10%) |
E |
| Sodium Hydroxide (50%) |
D |
| Sulfuric Acid (10%) |
C |
| Sulfuric Acid (70%) |
A |
| HCl (10% / aq) |
C |
| Acetic Acid (5%) |
B |
| |
|
|
|
| RECOMMENDED USES |
This system is primarily used for those applications where coatings must exhibit superior resistance to chemical exposure and material attack. Additionally, ProCote Bond/Base 2000 is also noted for outstanding abrasion resistance, high gloss, superior adhesion characteristics and decorative capabilities. |
| NOT RECOMMENDED FOR |
This system is not recommended for exterior use where high-gloss is desired due to the possibility of chalking. |
| INSTALLATION |
Installation is performed exclusively by our own factory-trained staff. Areas to be coated must be free of dirt, grease, oil, wax, and stripped of all previously applied coatings, sealants and curing compounds that are incompatible with this product. The application of a top coat is recommended to ensure proper sealing of the surface to be coated. |
|
| ProCote Top Coat Series II |
|
ProCote Top Coat Series II is a solvent based urethane top coat specially formulated for use on automotive floors where vehicles, equipment, and frequent oil and chemical exposure are present. This system exhibits excellent characteristics for impact resistance, abrasion resistance, chemical resistance, flixibility, weathering and UV stability. ProCote Top Coat Series II is a solvent-based urethane top coat available in clear or pigmented gloss finishes.
| PHYSICAL CHARACTERISTICS |
Abrasion Resistance
Tabor Abrasor using CS-17 calibrase wheel with 1000 gram total load for 500 cycles |
|
Flexural Strength
½" x ½" bars / span 4" |
|
Impact Resistance
Gardiner Variable Impactor (passed) |
50 in/lb
direct |
Yield Compressive Strength
½" x ½" bars |
9100 p.s.i. @ASTM D695 |
Tensile Strength
Testing directions: F=2.25", W=0.500", T=0.125", D=4.5" | Rate: 0.2"/min |
4800 p.s.i.
@ASTM D638 |
Ultimate Elongation
|
3.1%
|
Hardness
|
Shore D=80
|
Adhesion
No delamination (concrete failure) |
450 p.s.i. with alcometer |
Application Temperature
|
60-90° F
with relative humidity < 85% |
Viscosity
Typical, most colors |
1300-2300 cps
|
Pot Life |
30-50 mins
at 70° F |
Cure Schedule
Temperature at 70° F |
5-8 hours to Tack-Free
8-12 hours to Recoat
2-7 days to Full Cure |
| SPECIFYING INFORMATION |
Volatile Organic Content (VOC) |
Less than 3.8 per gallon |
Solids by Volume |
|
Solids by Weight |
|
Finish Characteristics
Erichsen glossmeter |
Gloss 70-95 at 60° |
| Mix Ratio |
2 : 1
Part A : Part B |
Recommended Film Thickness
|
3-5 mils wet |
| CHEMICAL RESISTANCE |
RATING KEY
| NOT RECOMMENDED |
A |
| 2 HR TERM SPLASH SPILL |
B |
| 8 HR TERM SPLASH SPILL |
C |
| 72 HOUR IMMERSION |
D |
| LONG TERM IMMERSION |
E |
| |
|
|
|
| Acetic Acid (5%) |
C |
| Xylene |
E |
| MEK |
B |
| Methyl Alcohol |
B |
| Gasoline |
D |
| Sodium Hydroxide (10%) |
E |
| Sodium Hydroxide (50%) |
D |
| Sulfuric Acid (10%) |
D |
| Hydrochloric Acid (10%) |
D |
| Nitric Acid (20%) |
C |
| Ethylene Glycol |
D |
| |
|
|
|
| RECOMMENDED USES |
This system is primarily used for those applications where coatings must exhibit superior resistance to chemical exposure and physical impact. Additionally, ProCote Top Coat Series II is also noted for outstanding abrasion resistance, light reflectancy, structural integrity and superior adhesion characteristics. |
| NOT RECOMMENDED FOR |
This system is not recommended for high-temperature applications such as metal torching and cutting facilities. Due to the self-leveling nature of this product, use is restricted to horizontal surfaces. |
| INSTALLATION |
Installation is performed exclusively by our own factory-trained staff. Areas to be coated must be free of dirt, grease, oil, wax, and stripped of all previously applied coatings, sealants and curing compounds that are incompatible with this product. |
|
| ProCote UltraLife |
|
ProCote UltraLife is a three-coat application of high-solid resin, vinyl loaded and textured to suit any desired finish requirements. Vehicle properties are obtained after curing of the mixed components. Chemical, impact and abrasion resistant surface film provides superior flexibility, weathering, and UV stability. UltraLife is available in a virtual unlimited array of color schemes and combinations.
| PHYSICAL CHARACTERISTICS |
Abrasion Resistance
|
|
Flexibility
|
|
Impact Resistance
|
Exceeds 160 in/lb
|
Pencil Hardness |
4H |
| Sward Hardness |
45 |
Cold Check Resistance
-40°F to 200°F per cycle |
Unaffected
25 cycles |
Weathering
Accelerated |
Unaffected
1000 hours |
Salt Spray
|
Unaffected
2000 hours |
Viscosity
Typical, most colors |
80-100 cps
|
Flash Point
Tag closed |
114°F |
Pot Life |
4 hours
at 70° F |
Drying Time
at 77°F |
6-8 hours to tack free
10-12 hours to recoat
|
Cure Schedule
Based on temperature |
7 days @ 77°F
2 hours @ 200°F
1 hour @ 250°F
30 mins @ 300°F |
| SPECIFYING INFORMATION |
Volatile Organic Content (VOC) |
Nearly zero pounds per gallon |
Solids by Volume |
|
Solids by Weight |
|
Finish Characteristics
Erichsen glossmeter |
Gloss
70-95 at 60° |
| Mix Ratio |
1 : 2
volume |
Film Thickness |
|
| CHEMICAL RESISTANCE |
KEY: R=RECOMMENDED FOR IMMERSION SERVICE; RS=RECOMMENDED FOR SPILLAGE ONLY; NR=NOT RECOMMENDED
ALKALIES
| Sodium Hydroxide (dilute) |
R |
| Sodium Hydroxide (concentrate) |
R |
| Calcium Hydroxide |
R |
| Ammonium Hydroxide (dilute) |
R |
| Ammonium Hydroxide (concentrate) |
RS |
| Ammonium Salts |
R |
| Sodium Carbonate |
R |
| |
|
ACIDS
| Sulfuric (10%) |
NR |
| Sulfuric (concentrate) |
NR |
| Hydrochloric (10%) |
RS |
| Hydrochloric (concentrate) |
RS |
| Nitric (10%) |
RS |
| Nitric (concentrate) |
NR |
| Phosphoric (10%) |
RS |
| Phosphoric (concentrate) |
NR |
| Hydrofluoric (10%) |
RS |
| Hydrofluoric (30%) |
NR |
| Lower Fatty, e.g. Acetic (20%) |
NR |
| Lower Fatty, e.g. Acetic (concentrate) |
NR |
| High Fatty, e.g. Oleic |
NR |
| Organic Food, e.g. Citric |
R |
| |
|
SOLVENTS
| Methylene Chloride |
NR |
| Other Chlorinated Hydrocarbons |
RS |
| Aromatic Hydrocarbons |
R |
| Aliphatic Hydrocarbons |
R |
| Alcohol (Methyl, Ethyl, & Butyl) |
R |
| Ether |
R |
| Esters |
RS |
| Ketones |
RS |
| Phenol |
RS |
| "Skydrol 500" |
R |
| |
|
HALOGENS
| Chloride |
NR |
| Bromine |
NR |
| Iodine |
NR |
| |
|
|
|
OXIDIZING AGENTS
| Hydrogen Peroxide (30%) |
NR |
| Sodium Hypochlorite (5%) |
R |
| Calcium Hypochlorite (5%) |
R |
| Chromic Acid (40%) |
NR |
| Chromic Acid (5%) |
NR |
| Sodium Dioxide Solutions |
NR |
| Chlorine Water |
R |
| |
|
WATER
SALT SOLUTIONS (5%-10%)
| Alum |
R |
| Ferrous Sulfate |
R |
| Copper Sulfate |
R |
| Sodium Chloride |
R |
| Calcium Chloride |
R |
| Sodium Sulfate |
R |
| Sodium Phosphate |
R |
| Sodium Acetate |
R |
| |
|
FATS AND OILS
| Mineral |
RS |
| Animal |
RS |
| Vegetable |
RS |
| |
|
GASES (MOIST)
| Carbon Dioxide |
R |
| Sulfur Dioxide |
R |
| Hydrogen Sulfide |
R |
| |
|
|
|
| RECOMMENDED USES |
This system is primarily used for those applications where coatings must exhibit superior resistance to chemical exposure and material attack. Additionally, ProCote Bond/Base 2000 is also noted for outstanding abrasion resistance, high gloss, superior adhesion characteristics and decorative capabilities. |
| NOT RECOMMENDED FOR |
This system is not recommended for exterior use where high-gloss is desired due to the possibility of chalking. |
| INSTALLATION |
Installation is performed exclusively by our own factory-trained staff. Areas to be coated must be free of dirt, grease, oil, wax, and stripped of all previously applied coatings, sealants and curing compounds that are incompatible with this product. The application of a top coat is recommended to ensure proper sealing of the surface to be coated. |
|
|
|
ProCote, D.M.S. | 1911 Bellaire, Royal Oak, MI 48067 | (800) 522-5425
©2007 ProCote, Dealer Maintenance Services. All rights reserved.
|
|
|